Effects of a cold atmospheric plasma device utilizing ambient air on bracket bonding to human enamel and surface roughness after debonding.

چکیده اصلی

OBJECTIVE: Evaluating a cold atmospheric plasma (CAP) device using ambient air for enamel pretreatment before bracket bonding and the impact on surface roughness. MATERIAL AND METHODS: 180 human third molars were assigned to 12 groups. After pretreatment with a) phosphoric acid+Transbond XT Primer (TXP), H₃PO₄, b) CAP (30 s)+TXP, CAP-30, c) CAP (60 s)+TXP, CAP-60, d) CAP+Transbond Plus self-etching primer (SEP-CAP) a metal bracket was bonded (Transbond XT adhesive). Shear bond strength (SBS) was tested after 1) 24 hours wet storage, 2) 500 thermal cycles (5°/55°C), 3) 90 days of wet storage with a universal testing machine. The adhesive remnant index (ARI) was determined. Additional specimens were fabricated, pretreated as groups a),b),d) before application of Transbond XT adhesive, removal with a tungsten bur and surface measurements before and after polishing with a profilometer. RESULTS: After 24 hours, SBS in the H₃PO₄ and SEP-CAP group was higher than in both CAP groups (p<0.001). 500 thermal cycles reduced SBS in both CAP groups compared to 24 hours (p<0.001) and 90 days (CAP-30 p=0.001; CAP-60 p=0.008). In both CAP groups, an ARI of 0 was predominant. Surface roughness before polishing was higher in the CAP group. CONCLUSIONS: The use of CAP with air as working gas does not ensure sufficient SBS for clinical use, but in combination with SEP. Surface roughness was more impacted by CAP than H₃PO₄. CLINICAL RELEVANCE: H₃PO₄ etching is still considered the gold standard for bracket bonding. Further research is required to understand the effect of CAP to enamel.

ترجمه فارسی چکیده

هدف: ارزیابی دستگاه پلاسما اتمسفر سرد (CAP) با استفاده از هوا برای پیش‌درمان مینا قبل از اتصال براکت و تأثیر آن بر خش‌خش سطح. مواد و روش‌ها: ۱۸۰ دندان سوم مغزی انسان به ۱۲ گروه تقسیم شدند. پس از پیش‌درمان با الف) اسید فسفریک + Transbond XT Primer (TXP)، ب) CAP (۳۰ ثانیه) + TXP، ج) CAP (۶۰ ثانیه) + TXP، د) CAP + Transbond Plus SEP-CAP، یک براکت فلزی متصل شد. استحکام برش (SBS) پس از ۱) ذخیره رطوبتی ۲۴ ساعته، ۲) ۵۰۰ چرخه حرارتی (۵/۵۵ درجه سانتی‌گراد)، ۳) ذخیره رطوبتی ۹۰ روزه با دستگاه تست جهانی اندازه‌گیری شد. شاخص باقیمانده چسب (ARI) تعیین شد. نمونه‌های اضافی با استفاده از بور تنگستن حذف و خش‌خش قبل و بعد از صیقل‌لی با پروفیلومتر اندازه‌گیری شد.

متن کامل اصلی